Article Sidebar
Published:
Jan 15, 2018DOI:
10.4314/njt.v36i4.17Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Hydrogenation of toluene on Ni-Co-Mo supported zeolite catalysts
Abstract
Mixed oxides of Ni, Co and Mo supported on five zeolites -ZSM-5-a, ZSM-5-b, HY-a, HY-b and Mordenite were prepared and characterized using many techniques for use as hydrotreating catalysts. In a preliminary investigation, toluene was employed as model compound to test the catalysts in hydrogenation, as a major upgrading reaction. TGA/DSC analysis showed that the impregnation of the metals slightly affected the thermal stability of the zeolites with all catalytic samples displaying good stability up to 730oC.The XRD patterns for all the catalytic samples showed that the framework of the zeolites were retained after impregnation. XRD and TPR results confirmed the presence of molybdenum trioxide on the zeolites with NiCoMo/HY-b displaying high metal-support interaction due to low reduction temperatures. The activity results showed that toluene conversion of almost 100% and selectivity to mainly methyl-cyclohexane was achieved. The catalysts activity test showed that the zeolite support textural properties particularly surface area, pore volume and pore diameter affect the performance of the catalysts. NiCoMo/HY-b displayed the best performance after the few minutes of the reaction due to its high surface area, pore volume and average pore diameter.
Keywords: Hydro treating catalysts; Hydrogenation; Toluene conversion; Surface area; Pore diameter