Article Sidebar
Published:
Nov 2, 2022DOI:
10.4314/njt.v41i3.3Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Assessment of crystallite phase, morphology and mechanical properties of concrete reinforced with polyethylene terephthalate (PET)/carbon nanotubes (CNTs)
Abstract
PET (Polyethylene terephthalate) is a semicrystalline thermoplastic polymer with good chemical resistance, thermal stability, melt mobility, and spinnability. In recent years, the development of nanocomposites with various types of nanomaterials has become a fascinating topic in material science. The polyethylene terephthalate (PET) blended with carbon nanotubes (CNTs) was mixed with concrete to prepare concrete/PET/CNTs nanocomposites. The PET/CNTs were employed as reinforcing material to study the synergistic effect between PET/CNTs and concrete. The impact of PET/CNTs at different ratios on the crystallite phase and morphology of the materials was examined using X-ray diffraction spectroscopy (XRD) and high-resolution scanning electron microscopy (HRSEM), respectively. The mechanical properties were tested using tensile, compression, and flexural measurement. The presence of PET/CNTs changes the orientation of minerals, thus reducing the crystallite sizes in the matrices at a higher amount of PET/CNT. The excellent mechanical strength of the composite materials gradually increased with the increase in concrete/PET/CNTs. The concrete/PET/CNT (1:4) performance was far from rutting due to the excellent compatibility and crosslinking between the reinforcing material and the concrete, thus increasing the mechanical strength and improving the resistance to cracking.